| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM |
| Grade: | 300 Series |
|
Still deciding? Get samples of US$ 50/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Products | Stainless Steel Round Bar |
| Grade | 321 / 1.4541 / UNS S32100 |
| Standard | ASTM A276/276M |
| Diameter | 8 - 300mm |
| Length | 6m/pcs or cutting any length as request |
| Surface | black, bright |
| Other Grade | 304 310S 316L 317L 321 410 420 431 440A/B/C 2205 2507 630 631 904L.etc |
| Service | Cutting, polishing, heat treatment |
| Products Name | Size Range | Mainly Grade |
| Stainless Steel Round Bar (hot rolled black surface) | 8 - 300mm | 304 304L 309S 310S 316L 316Ti 317L 321 347 410 420 431 440A/B/C 2205 2507 904L 254SMO 17-4PH 17-7PH.etc |
| Stainless Steel Round Bar (bright polished) | 3 - 50mm | 201 304 316L 310S 2205 630.etc |
| Stainless Steel Square Bar | 4*4 - 50*50mm | 201 304 316L 310S 410 420 .etc |
| Stainless Steel Hexagon Bar | S4-S70 | 201 304 316L 310S 410 420 .etc |
| Stainless Steel Flat Bar | 10*3 - 100*40 | 304 304L 309S 310S 316L 316Ti 317L 321 347 410 420 431 440A/B/C 2205 2507 904L 254SMO 17-4PH 17-7PH.etc |
| Stainless Steel Angle Bar | 30*30 - 200*200 | 201 304 316L 310S 2205.etc |
| Stainless Steel Channel Bar | 50*25 - 200*100 | 201 304 316L 310S 2205.etc |
Alloy 321 (UNS S32100) is stabilized stainless steel plate which offers as its main advantage an excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800 to 1500°F (427 to 816°C). Alloy 321 stainless steel plate is stabilized against chromium carbide formation by the addition of titanium.
Alloy 321 stainless steel plate is also advantageous for high temperature service because of its good mechanical properties. Alloy 321 stainless steel plate offers higher creep and stress rupture properties than Alloy 304 and, particularly, Alloy 304L, which might also be considered for exposures where sensitization and intergranular corrosion are concerns.
Alloy 321 (UNS S32100) is titanium stabilized austenitic stainless steel plate with good general corrosion resistance. It has excellent resistance to intergranular corrosion after exposure to temperatures in the chromium carbide precipitation range of 800 - 1500°F (427 - 816°C). The alloy resists oxidation to 1500°F (816°C) and has higher creep and stress rupture properties than alloys 304 and 304L. It also possesses good low temperature toughness.
Alloy 321H (UNS S 32109) stainless steel plate is the higher carbon (0.04 - 0.10) version of the alloy. It was developed for enhanced creep resistance and for higher strength at temperatures above 1000oF (537°C). In most instances, the carbon content of the plate enables dual certification.
Alloy 321 stainless steel plate cannot be hardened by heat treatment, only by cold working. It can be easily welded and processed by standard shop fabrication practices.
Typical compositional ranges for grade 321 stainless sheets of steel are given in table 1.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 321 | min. max |
- 0.08 |
2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 |
- | 9.0 12.0 |
0.10 | Ti=5(C+N) 0.70 |
| 321H | min. max |
0.04 0.10 |
2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 |
- | 9.0 12.0 |
- | Ti=4(C+N) 0.70 |
| 347 | min. max |
0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0 19.0 |
- | 9.0 13.0 |
- | Nb=10(C+N) 1.0 |
Typical mechanical properties for grade 321 stainless sheets of steel are given in table 2.
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50 mm) min | Hardness | |
|---|---|---|---|---|---|
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 321 | 515 | 205 | 40 | 95 | 217 |
| 321H | 515 | 205 | 40 | 95 | 217 |
| 347 | 515 | 205 | 40 | 92 | 201 |
Typical applications include: