| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM, AISI |
| Grade: | 300 Series |
| Certification: | AISI |
| Shape: | Flat |
| Technique: | Hot Rolled |
| Samples: |
|---|
Suppliers with verified business licenses
Audited Supplier Stainless steel grade 314 has excellent high-temperature resistance characteristics among the chromium-nickel steels series. The silicon content in this material improves oxidation and carburization resistance; however, it can become very brittle when subjected to prolonged temperatures of 649-816°C (1200- 1500°F).
Hot Rolled 314 Stainless Steel Plate 310SSi2 Heat Resistant SS Plate 3.0 - 20mm TISCO NO.1
| ITEM | 314 Stainless Steel Sheet | ||
| BRAND | TISCO | ||
| Size | 3 - 20mm*1500*6000mm | ||
| STANDARD | JIS ASTM DIN | ||
| CERTIFICATE | ISO | ||
| SURFACE | NO.1 | ||
| PACKING | Standard export sea-worthy packing | ||
| SHIPMENT | Ocean shipping | ||
| LEAD TIME | 10-15 days after deposit | ||
| PAYMENT | T/T, L/C, Western Union | ||
Stainless steel grade 314 has excellent high-temperature resistance characteristics among the chromium-nickel steels series. The silicon content in this material improves oxidation and carburization resistance; however, it can become very brittle when subjected to prolonged temperatures of 649-816°C (1200- 1500°F).
Chemical composition of the 314
| C ≤ |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni |
|---|---|---|---|---|---|---|
| 0.25 | 1.50-3.00 | 2.00 | 0.045 | 0.030 | 23.0-26. | 19.0-22.0 |
Mechanial Properties of the 314
| Yield Rp0.2(MPa) |
Tensile Rm(MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 272 (≥) | 549 (≥) | 13 | 43 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 |
Equivalent materials to grade 314 stainless steel are given below.
| AFNOR Z 12 CNS 25.20 | DIN 1.4841 | UNI X 16 CrNiSi 25 20 | UNI X 22 CrNi 25 20 | JIS SUS Y 31O |
| B.S. 310 S 24 | AMS 5522 | AMS 5652 | ASTM A276 | ASTM A314 |
| ASTM A473 | ASTM A580 | SAE 30314 | SAE J405 (30314) |
Stainless steel grade 314 can be heat treated by annealing the material at 1038-1149°C (1900-2100°F), and then quenching in water or rapidly air cooling. Grade 314 steel can be hardened only through cold working. To perform machinability of grade 314, coolant and high-speed turning tools are recommended.
After slowly heating the material to 871°C (1600°F), it should be thoroughly soaked, and then followed by quickly heating to 1093 -1232°C (2000-2250°F) , to perform forging, flanging, or working.
Grade 314 steel is widely used in the following applications:
We can also supply other similar grade of stainless steel, following the detail informations:
| Products | stainless steel plate | ||
| Manufacturer | TISCO BAOSTEEL JISCO | ||
| Thickness | CR: 0.6 - 3.0mm HR: 3.0 - 80mm | ||
| Size | CR 1219*2438mm HR: 1500*6000mm | ||
| Surface | CR : 2B HR: No.1 | ||
| Grade | 304 316L 309S 310S 321 2205 | ||
| Stock | have stock, total 300 Tons in stock | ||
| Loading port | Shanghai,China | ||
Chemical Composition
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 689 MPa | 99900 psi |
| Yield strength | 345 MPa | 50000 psi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Elongation at break (in 50 mm) | 40% | 40% |
| Hardness, Rockwell B | 85 | 85 |
Grade 314 steel is widely used in the following applications: