410 stainless steel properties
Type 410 SS is a hardenable, martensitic stainless steel. It combines the superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless. It features high strength, heat resistance, and good ductility. Good corrosion resistance in mild atmospheres, steam and mild chemical environments make it well suited for highly stressed parts. This grade of 410 stainless steel is magnetic in both the annealed and hardened conditions.
Our 410 stainless steel materials are used in aerospace, automotive, petrochemical and medical applications. Grade 410 SS is also used in manufacturing of products like springs and fasteners, as it can be machined after tempering or annealing. For free machining applications that do not require the higher corrosion resistance of 410, consider our grade of 416 stainless instead.
410 stainless steel Standard Inventory Specifications
UNS S41000 AMS 5504 AMS 5613 (Chemistry only)
ASTM A 240 ASTM A 276 ASTM A 493
ASTM F 899 ASME SA 240 B50991B
|
Element |
Percent by Weight |
|
|---|---|---|
|
C |
Carbon |
0.15 max |
|
Mn |
Manganese |
1.00 max |
|
Si |
Silicon |
1.00 max |
|
Cr |
Chromium |
11.50 - 13.50 |
|
C |
Nickel |
0.75 max |
|
S |
Sulfur |
0.03 max |
|
P |
Phosphorus |
0.04 max |
The values reported below are typical for Type 410 alloy in the annealed condition.
Density: 0.276 lb/in3
Specific Gravity: 7.65
Melting Range: 2700-2790°F 1482-1532°C
Modulus of Elasticity: 29 x 106 psi (200 GPa)
|
Temperature Range |
Coefficients |
||
|---|---|---|---|
|
°C |
°F |
cm/cm/°C |
in/in/°F |
|
20-200 |
68-392 |
10.5 x10-6 |
5.9 x 10-6 |
|
20-600 |
68-1112 |
11.6 x 10-6 |
6.5 x 10-6 |
|
Temperature Range |
W/m·K |
Btu/(hr · ft · °F) |
|
|---|---|---|---|
|
°C |
°F |
||
|
100 |
212 |
(0.249) |
14.4 |
410 stainless steel Specific Heat
.11 Btu/lb.·°F
|
Temperature Range |
microhm-cm |
|
|---|---|---|
|
°C |
°F |
|
|
20 |
68 |
56 |
410 stainless steel Mechanical Properties and Yield Strength
|
Typical Annealed Properties |
Hardening Response HRC |
|||
|---|---|---|---|---|
|
HRB |
0.2% Offset |
Tensile Strength |
Elongation, Percent in 2" (51 mm) |
|
|
82-96 |
30 (205) - 42 (290) |
65 (450) - 74 (510) |
20 -34 |
38-45 |
410 stainless steel Common Trade Names
ATI 410 (™ Allegheny Technologies)
Alloy 410
AISI Type 410
410 stainless steel Common Applications
Aerospace structures
Automotive exhausts, manifolds and high temperature engine components
Medical instruments and devices
Petro-chemical applications
Cutlery, kitchen utensils
Flat springs
Hand tools