Introduction:
Grade 1.6511 / SAE4340 has the characteristic of high strength, toughness and good hardenability and anti-overheating stability, but the white point sensitivity is high, and there is temper brittleness.The welding property is poor, before welding, it needs to be preheated by high temperature. After welding, the stress should be eliminated and used after adjustment.
Chemical composition(%):
C | Si | Mn | S | P | Cr | Mo | Ni |
0.38~0.43 | 0.15~0.35 | 0.60~0.80 | ≤0.040 | ≤0.035 | 0.70~0.90 | 0.20~0.30 | 1.65~2.00 |
Application:
Used as require good toughness, high strength, as well as the important conditioning of large size, heavy machinery such as high load of axial, turbine shaft, larger than 250 mm in diameter of helicopter rotor shaft, turbojet engine turbine shaft, blade, high load of transmission parts, fasteners of the crankshaft,gear, etc.
It can also be used for operating temperature over 400 ºC of rotor shaft and blade, etc. and after nitriding processing can also be used to make special performance requirements of the important parts, after low temperature tempering or can be used for ultra-high strength steel after thermal quenching.
Features:
Excellent hardenability, high toughness and good heat-resistance and fatigue-resistance.
Heat treatment:
Quenching | Tempering | ||
Heating temperature/ºC | Cooling | Heating temperature/ºC | Cooling |
850 | Oil cooling | 600 | Water or oil cooling |
Hardness | ≤269HB |
Mechanical properties:
Tensile strength sigma b (MPa): ≥980(100),
The elongation is delta 5 (%): ≥12,
The cross-sectional shrinkage of psi (%): ≥55.
Impact work Akv (J) is greater than 25, impact toughness value alpha kv (J/cm2): ≥98 (10).
Delivery time:
Hot rolled or forged, black surface.
For abundant stock, 15-20 days.For customized products, 30-50 days.
Our main products | |
Platic mould steel: |
S50C, P20, P20+Ni, P21, 420 |
Hot work mould steel: | H13/1.2344, H21/1.2581 |
Cold work mould steel: | D2, D3, O1/1.2510 |
Alloy steel: | 1.7035, 1.7225, En31, 1.6523 |
High speed steel: | M2/1.3343, T1/1.3355, M35, M42 |
Product products:
Hot sale products for plastic mould Steel | |||||||||
STANDARD/GRADE | Steel Plate Size(mm) | Round bar Size(mm) | Technics | ||||||
DIN | AISM | JIS | GB(China) | Thickness | Width | Length | Diameter | Length | |
1.1210 | SAE1050 | S50C | 50# | 10-1000 | 155-2200 | 3000-6000 | 10-350 | 3000-6000 | Hot Rolled |
1.1191 | SAE1045 | S45C | 45# | 10-700 | 155-2200 | 3000-6000 | 10-300 | 3000-6000 | |
1.2311 | P20 | PDS-3 | 3Cr2Mo | 12-800 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | Forged, Hot Rolled |
1.2738 | P20+Ni | - | 3Cr2NiMnMo | 21-1000 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | |
1.2083 | 420 | - | 4Cr13 | 12-500 | 155-1200 | 2000-6000 | 12-300 | 3000-6000 |
Hot sale products for hot / cold work mould Steel | |||||||||
STANDARD/GRADE | Steel Plate Size(mm) | Round bar Size(mm) | Technics | ||||||
DIN | AISM | JIS | GB(China) | Thickness | Width | Length | Diameter | Length | |
1.2344 | H13 | SKD61 | 4Cr5MoSiV1 | 16-500 | 155-500 | 2000-6000 | 16-200 | 3000-6000 | Forged, Hot Rolled |
1.2379 | D2 | SKD10 | SKD10 | 6-200 | 155-810 | 2000-6000 | 10-180 | 3000-6000 | |
1.2080 | D3 | SKD1 | 3Cr2Mo | 10-200 | 155-810 | 2000-6000 | 10-180 | 3000-6000 | |
1.2510 | O1 | SKS3 | 9CrWMn | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 |