Heat Resistant TP310S Grade Seamless Austenitic Stainless Steel Pipes for Boiler
Specification of our stainless steel pipe
| Products Name | Stainless Steel pIpe |
| Diameter | DN6 - DN500 |
| Wall Thickness | SCH10S - XXS or unstandard size as request |
| Length | 6m or cutting any length as request |
| Standard | ASTM JIS EN DIN |
| Technique | Hot Rolled / cold drawn |
| Type | Seamless Pipe / Welded Pipe |
| Surface | Bright Polished, Pickling |
| Main Grade | 201 304 304L 309S 310S 316L 316Ti 316LMod 317L 321 347 410 904L 254SMO 253MA 2205 2507 654SMO 926 400 c276 c22 C4 600 625 800 825.etc |
| MOQ | 500 kgs |
| Loading Port | Shanghai Port |
| Packing | wooden box or ppbag |
About 310S Stainless Steel
Alloy 310 is an austenitic stainless steel that combines excellent high temperature properties with good ductility and weldability. It is typically used for elevated temperature applications as its high chromium and nickel content provide solid corrosion resistance, excellent resistance to oxidation, and superior strength in temperatures up to 2100°F. Due to its high chromium and nickel content, it is superior to 304 or 309 stainless in most environments.
PRODUCT DESCRIPTION
TP310S Seamless Pipe Chemical Composition:
| HEAT NO. | Chemical Composition (%) | |||||||||||
| C | Mn | P | S | Si | Ni | Cr | Mo | |||||
| STAND. | MIN. | 19.00 | 24.00 | |||||||||
| MAX. | 0.080 | 2.00 | 0.045 | 0.030 | 1.00 | 22.00 | 26.00 | 0.75 | ||||
TP310S Seamless Pipe Mechanical Properties:
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) | Brinell (HB) | ||||
| TP310S | 515 | 205 | 35 | 90 | 187 |
Application of 310S Stainless Steel Pipe
The higher alloyed stainless steels generally have excellent strength at elevated temperatures along with outstanding resistance to creep deformation and environmental attack. Therefore, Alloy 310 is used widely in industries such as heat treatment and chemical processing. Some examples include: