| Type: | Stainless Steel Sheets |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 300 Series |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Products | Stainless Steel Plate |
| Thickness | 0.4 - 40.0mm |
| Width | 1000mm 1219mm 1500mm 1800mm 2000mm or other width as request |
| Length | 2000mm 2438mm 3000mm 6000mm or other length as request |
| Grade | 201 202 301 304 304L 304H 309S 310S 316L 316Ti 317L 321 347 409L 410 420 430 431 434 436L 439 441 443 444 2205 2507 904L 600 625 800 825 718 253MA 254SMO.etc |
| Service | Laser Cutting, Surface processing, bending |
| Brand | TISCO BAOSTEEL POSCO LISCO JISCO |
| Standard | ASTM JIS GB DIN EN BS |
| Certificate | ISO MTC C/O F/E |
| Packing | Wooden pallets and waterproof paper |
| Deliver time | 5 - 15 days |
| Loading port | Shanghai Port |
Super-austenitic stainless steels cover grades with high chromium (20 to 27 %), high nickel (18 to 31 %) and high molybdenum (4 to 6 %) contents. Within this family, the 6%Mo high nitrogen grade S31266 was developed to combine the beneficial influence of chromium, tungsten, molybdenum and nitrogen on its mechanical and corrosion properties. Due to 22 % nickel, 24 % chromium and 0.4 % nitrogen additions, this alloy exhibits a very stable microstructure, being less prone to intermetallic phase precipitation than the other highly alloyed super-austenitic stainless steels.
This paper deals with the corrosion resistance of S31266 in artificial geothermal water with moderate salinity and low pH. Long-term static exposures and electrochemical tests were conducted at various temperatures to evaluate the pitting, crevice and stress corrosion cracking resistance of this material.
The results show that S31266 is resistant up to 220 °C. As a consequence, it can be a good candidate material for geothermal applications involving a highly corrosive environment, especially salinity and low pH.
Chemical Composition of UNS S31266 Stainless Steel
| C | Mn | P | S | Si | Ni | Cr | Mo | Cu | N |
| 0.02 | 2.00 | 0.04 | 0.03 | 1.00 | 23.0-28.0 | 19.0-23.0 | 4.0-5.0 | 1.00-2.00 | 0.10 |
Mechianical Properties of UNS S31266 Stainless Steel
| Tensile Strength/Mpa .min | Yield Strength / Mpa.min | Elongation.min | Reducer Area.min |
| 750 | 420 | 35 | 50 |
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.