We are a GB 65Mn steel stockholders and China suppliers. And Mittel Steel supplly in GB 65Mn Spring Steel round bar, flat bar., rod bar, wire and plate supply.
Moreover, GB 65Mn Steel is a high quality Alloy Spring Steel, and it belong to the high quality high carbon alloy Spring Steel.Its Quenched & Tempered Hardness is 28-34 HRC. 65Mn steel under Annealing delivery hardenss less than 250HB.
Related Specifications ASTM A29/A29M DIN EN 17221 JIS G4801 GB GB/T 1222 GB 65MN Spring Steel Date PDF DOWN
Form of Supply
GB 65Mn Spring Steel China Supplier and Stockist, and Otai Special Steel can supply the round bar, steel flat bar, plate, hexagonal steel bar and steel square block. AISI 65Mn steel Round bar can be saw to your required lengths as one offs or multiple cut pieces. 65Mn steel Rectangular pieces can be saw from flat bar or plate to your specific sizes. And Ground Spring Steel bar can be supplied, providing a quality precision finished bar to tight tolerances.
Round
sheet
Square
Plate
Chemical composition
| C(%) | 0.62-0.70 | Si(%) | 0.17-0.37 | Mn(%) | 0.90-1.20 | P(%) | ≤0.035 |
| S(%) | ≤0.035 | Cr(%) | 0.25max | Ni(%) | 0.25max |
Equivalent Of 65Mn alloy Spring Steel
| USA | Germany | China | Japan | France | England | Italy | Poland | ISO | Austria | Sweden | Spain |
| AISI/SAE/ASTM/UNS | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | ISO | ONORM | SS | UNE |
| 1066 | 65Mn | 080A67 | |||||||||
Heat treatment Related
- Annealing of 65Mn Spring Steel
At first Slowly heated to 730 ºC and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. Then 65Mn tool steel will get MAX 250 HB (Brinell hardness).
- Hardening of 65Mn Spring Steel
At the beginning, 65Mn steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. After about 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil. Tempering of 65Mn Spring Steel
Tempering of 65Mn steels is performed at 540°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Hardness values at different temperatures after tempering
Mechanical Properties
The mechanical properties of 65Mn Spring Steels are outlined in the following table.
| Tensile strength | Conditions to yield strength | Elongation | Reduction of area | Hardness (Hot Rolled) | Hardness (Cold Drawn) |
| σb (MPa):≥980 | σ0.2 (MPa):≥785 | δ 5 (%):≥8 | ψ (%):≥30 | ≤302HB; | |
Applications
65Mn steel, after heat treatment and cold drawing hardening, high strength, it has a certain toughness and plasticity; In the same surface hardening case, completely and the fatigue limit and alloy spring. But hardenability poor, mainly for the smaller size of the spring, such as regulating speed regulating spring, spring load, general machinery in the round, square spiral spring or pull wire for small mechanical spring.
Regular size and Tolerance
Steel round bar: Diameter Ø 2mm - 3000mm
Steel plate: Thickness 2mm - 3000mm x Width 100mm - 3500mm
Steel Hexagonal bar: Hex 5mm - 105mm
Others 65Mn have not specified size, pls contact our experienced sales team.
Processing
Moreover, GB 65Mn Spring Steel round bar and flat sections can be cut to your required sizes. 65Mn Spring Steel ground bar can also be supplied by us, providing a high quality Spring Steel precision ground Spring Steel bar to your required tolerances. And GB 65Mn steel is also available as Ground Flat Stock / Gauge Plate, in standard and nonstandard sizes.
Contact our experienced sales team to help you with your 65Mn Spring Steel questions and enquiry by Email or Telephone. The questions will be reply in 24 hours.