N08020 is a low-carbon, niobium-stabilized austenitic nickel/iron/chromium alloy with additions of molybdenum and copper. It exhibits exceptional corrosion resistance in chemical environments containing phosphoric acid, chlorides and sulfuric acid. It also has good mechanical properties at both ambient and elevated temperatures.
The following sections will discuss in detail about N08020
The chemical composition of N08020 is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 35 |
| Nickel, Ni | 32-38 |
| Chromium, Cr | 19-21 |
| Copper, Cu | 3-4 |
| Manganese, Mn | ≤2 |
| Molybdenum, Mo | 2-3 |
| Niobium, Nb | ≤1 |
| Silicon, Si | ≤1 |
| Carbon, C | ≤0.07 |
| Phosphorous, P | ≤0.045 |
| Sulfur, S | ≤0.035 |
The following table shows the physical properties of N08020
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.05 g/cm3 | 0.291 lb/in3 |
The mechanical properties of N08020 are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (annealed) | 620 MPa | 89900 psi |
| Yield strength (annealed) | 300 MPa | 43500 psi |
| Elongation at break (annealed) | 41% | 41% |
The thermal properties of N08020 are given in the following table
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 14.7 µm/m°C | 8.17 µin/in°F |
| Thermal conductivity | 12.3 W/mK | 85.4 BTU.in/hrft².°F |