High Quality 316lmod Stainless Steel Round Bar Urea Grade Stainless Steel Bar

• Type: Stainless Steel Bars
• Standard: GB, JIS, DIN
• Grade: 300 Series
• Certification: ISO, RoHS, ASTM, EN, JIS
• Shape: Round
• Technique: Hot Rolled
• Model NO.: 316LMod
• Surface Treatment: Pickling
• Length: 6m or Cutting Any Length as Request
• Service: Cutting, Heat Treatment
• Products Bame: 316lmod Stainless Steel Bar
• Other Grade: 200 Series 300 Series 400 Series
• Transport Package: Wooden Box
• Specification: 4 - 350mm
• Origin: China
• Production Capacity: 100000 PCS / Year

Product Description

 

High Quality 316LMod Stainless Steel Round Bar Urea Grade Stainless Steel Bar 
 

Product Description

                                                                                                                                                        Urea Grade 316LMod Stainless Steel Bar Diameter 6 - 250mm Hot Rolled / Forged SS Bars

316LMOD Urea Class Stainless Stee                                   l

                    UREA 316L Modified grade has been specially developed for Urea plant applications. It is a 316L modified stainless steel with extra-low silicon content and substantial higher molybdenum contents.

                                                                                                                                    
The low carbon content, combined with a well balanced chemistry (low silicon and nickel content close to 14%) makes the alloy fully austenitic, free of intermetallic phase precipitations. The ferrite level is kept under 0.5% in the solution annealing and water quenched conditions.
The alloy is designed for improved corrosion resistance properties in Urea- carbonate environments.

                                                                         
316LMod material is specially developed for Urea plant applications. It is a 316L modified stainless steel with extra-low silicon content and substantial higher molybdenum contents. The low carbon content, combined with a well balanced chemistry (low silicon and nickel content close to 14%) makes the alloy fully austenitic, free of intermetallic phase precipitations. The ferrite level is kept under 0.5% in the solution annealing and water quenched conditions. The alloy is designed for improved corrosion resistance properties in Urea-carbonate environments.


Products Specification of 316LMod Stainless Steel Bar

 

Products Name	316LMod Stainless Steel Round Bar
Diameter	6 - 250mm
Length	6m or cutting any length as request
Products Type	cold drawn , hot rolled , forged
Surface	bright, black ,
Other grade	201 202 301 303 304L 304 309S 310S 316L 316Ti 316LMod 317L 321 347 410 420 430 431 434 440A/B/C  2205 2507 904L 254SMO 253MA
Brand	BAOSTEEL WALSIN DELTA GMS
Service	cutting , polishing , heat treatment
MOQ	500 kgs
Loading Port	Shanghai Port
Deliver time	5 - 12 days for regular size
Packing	wooden box or packing as request

 

FEATURE PRODUCTS

 

Chemical Composition of 316LMod Stainless Steel

%	C	Mn	P	S	Si	Cr	Ni	Mo	Cu	N	Fe
Min	-	1	-	-	-	17	13	2.2	-	-	balance
Max	0.03	2	0.04	0.03	0.5	18.5	15	3	-	0.22	balance

Mechanical Property of 316LMod Stainless Steel

20°C	Tensile Strength	Yield Strength	Elongation %	Hardness	Density
Min	490Mpa	190Mpa	35%	-	7.9kg/dm3
Max	-	-	-	90HRB	7.9kg/dm3

Grade Specification of 316LMod Stainless Steel 


EN 10088 / EN 10028 ......... X2 Cr Ni Mo 18-14-3 - 1.4435
AFNOR................................Z3 CND 18.14.03
DIN...................................... W.Nr 1.4435
ASTM. ............................... 316L modified


Hot forming


Hot forming should be carried out in a temperature range of 1200-950C (2732- 1742F) after the piece has been uniformely heat treated. Final full annealing tremperature is required to obtain the requested microstructure. It will be performed at 1120-1180C (2048-2156F) followed by water quenching.


Cold forming


Due to its fully austenitic microstructure, the alloy can be cold formed without any problem. The higher molybdenum content and cold hardening behaviour of the steel explains that it may require more powerfull equipments than 304 stainless steel.


Pickling


The UREA Modified grade must be used in the as pickled and passivated conditions. Pickling treatment may be performed with a nitro-hydrofluoric acid bath (10-20 % HN03 - 1.5-5% HF) at room temperature (few hours) or 20 minutes approx. at 60C (140F). 10-20% H2SO4 - 1.5-5% HF pickling bath may also be used.
Alloy UREA Modified can be welded with most of the welding processes : TIG, Plasma, MIG welding, as well as SMAW, SAW or FCAW processes.
The alloy is sensitive to hot cracking phenomenon due to its fully austenitic microstructure.
Weld should be performed in order to obtain extra-low ferrite contents, no carbide or nitrides precipitations, low silicon contents as well as no intermetallic phases precipitations.
Higher manganese content products should be considered.


Use basic coated electrodes or fluxes in order to decrease the hot cracking susceptibility. The heat input should be limited to 1,5 kJ/mm and interpass temperature kept below 150C (302F).
Typical corrosion test results in Huey test solution - ASTM A262-C are as follow :
maxi weight loss 3.3 m/48h - 0,54 g/m h with selective attack lower than 200 m.

Detailed Photos